PA6 ST811HS BK038 Zytel 韌(ren)性(xing)良好擠齣

PA6 ST811HS BK038 Zytel 韌(ren)性良好擠齣

PA6 ST811HS BK038 Zytel  物(wu)性錶: 

流變性能(Rheological properties) dry / cond 單位(Unit) 測(ce)試標準(Test Standard)

ISO數(shu)據

成型收縮(suo)(Molding shrinkage) (parallel) 0.9 / * % ISO 294-4, 2577

成(cheng)型(xing)收縮(Molding shrinkage) (normal) 1.4 / * % ISO 294-4, 2577

機械(xie)性能(機械性能(neng)(Mechanical properties)) dry / cond 單位(Unit) 測試(shi)標準(Test Standard)

ISO數據

拉伸糢量(Tensile Modulus) 850 / - MPa ISO 527-1/-2

斷(duan)裂拉伸應變(Nominal strain at break) >50 / - % ISO 527-1/-2

破壞時(shi)應變(Stress at break) 44 / - MPa ISO 527-1/-2

破壞時(shi)應變(bian)(Strain at break) >50 / - % ISO 527-1/-2

簡(jian)支樑衝擊強度(Charpy impact strength) (+23°C) N / - kJ/m² ISO 179/1eU

簡支樑缺口衝擊強(qiang)度(Charpy notched impact strength) (+23°C) 80 / - kJ/m² ISO 179/1eA

彎麯彈性(xing)糢量(Flexural modulus) (23°C) 850 / - MPa ISO 178

懸臂樑式衝擊切(qie)口 (23°C) 65 / - kJ/m² ISO 180/1A

懸臂樑式衝擊切口 13 / - kJ/m² ISO 180/1A

溫度(du)(Temperature) -40 °C ISO 180/1A

懸臂樑式衝擊無切(qie)口(kou)(Izod Impact unnotched) (23°C) N kJ/m² ISO 180/1U

熱性能(neng)(熱性能(Thermal properties)) dry / cond 單位(Unit) 測試(shi)標準(zhun)(Test Standard)

ISO數據

熔化溫度(熔(rong)化溫度(Melting temperature)) (10°C/min) 218 / * °C ISO 11357-1/-3

溫度負(fu)荷變形(Temp. of deflection under load) (1.80 MPa) 40 / * °C ISO 75-1/-2

溫度負荷變形(Temp. of deflection under load) (0.45 MPa) 85 / * °C ISO 75-1/-2

COEFF線性(xing)熱(re)(Coeff. of linear therm. expansion) (parallel) 130 / * E-6/K ISO 11359-1/-2

COEFF線性熱(Coeff. of linear therm. expansion) (normal) 140 / * E-6/K ISO 11359-1/-2

其他屬(shu)性(Other properties) dry / cond 單位(Unit) 測試標準(Test Standard)

ISO數據(ju)

密度(Density) 1050 / - kg/m³ ISO 1183

CharacteristicsProcessingInjection Molding, Other ExtrusionDelivery formPellets, BlackAdditivesLubricantsSpecial CharacteristicsHigh impact or impact modified, Heat stabilized or stable to heatApplicationsAutomotive, Electrical and Electronical, Sports EquipmentRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaDisclaimerCopyright M-Base .